Applied Sciences (Switzerland), cilt.16, sa.7, 2026 (SCI-Expanded, Scopus)
Background and Objectives: Soft denture lining materials improve stress distribution and patient comfort but can lose mechanical stability under routine chemical cleansing. This study aimed to evaluate the time-dependent effects of two alkaline peroxide-based denture cleansing tablets (i.e., Efferdent and Protefix) on Shore A hardness and weight change of three soft lining materials (i.e., Ufi Gel P, Ufi Gel SC, and Visco-gel) at days 1, 7, and 30. Materials and Methods: Ninety specimens (n = 10/group) were assigned to a 3 × 3 factorial design. Specimens were immersed in cleansing solutions for 8 h daily and stored in artificial saliva for 16 h; controls remained solely in artificial saliva. Shore A hardness was measured using a durometer, and weight was recorded with a precision scale. Data were analyzed by mixed-design ANOVA and linear regression (α = 0.05). Results: Material type significantly affected hardness and weight change (p < 0.001). Visco-gel showed a marked increase in Shore A hardness (from about 15–16 to 26–27 HA) and greater weight loss (approximately 0.04–0.06 g), whereas silicone-based materials (Ufi Gel P and Ufi Gel SC) demonstrated more stable hardness values (from about 24–25 to 31–32 HA) with minimal weight variation (generally below about 0.02 g). The type of cleansing tablet had a smaller but significant effect (p = 0.004), with Protefix causing greater alterations. Weight change was negatively correlated with hardness increase (R2 = 0.33, p < 0.001). Conclusions: Within the limitations of this in vitro study, material composition was identified as the main determinant of degradation resistance, with silicone-based liners demonstrating greater durability under the tested conditions, while Efferdent may be considered a milder option for long-term cleansing.